Only by knowing the influence of welding pressure on welding can we better operate and adjust the high frequency straight seam welded pipe unit to achieve higher efficiency. Today let's take a look at the effect of welding pressure on the high frequency straight seam welded pipe machine.
Welding pressure is also the main parameter of high frequency welding.
Theoretical calculations suggest that the welding pressure should be 100~300MPa, but the actual pressure in this area is difficult to measure in actual production. It is generally estimated based on experience and converted into the amount of extrusion at the edge of the tube.
Different wall thickness takes different extrusion amount, usually the extrusion amount below 2mm is:
0.5t~t for 3~6 mm; 0.5t for 6~10 mm; 0.3t~0.5t for over 10 mm.
In the production of API steel pipes, there are often gray spot defects in welds, which are refractory oxides. The extrusion allowance of steel pipes above 6mm is 0.8~1.0 material thickness, and the effect is very good.
TENGDI MACHINERY Specializing in the design and manufacture of various types of high-frequency welded pipe units, stainless steel precision welded pipe units, high-precision steel-plastic, stainless steel composite welded pipe units; design and manufacture of various specifications and types of welded pipe molds - rolls, special-shaped rollers, so that the products have formed a series, It enjoys a high reputation among domestic and foreign merchants.
For more information, please consult:
www.tengdimc.com admin@tengdimc.com
The appearance of gaps refers to the phenomenon that the welds are not bonded together. The length of the gaps is generally more than a few centimeters or even longer. The main reasons are as follows:(1) Pass wearAs the extrusion roll hole pattern wears, the hole pattern (R) size gradually becomes l
Sand-hole pipes are also a kind of quality accident caused by weld leakage, but their gaps are very small, some of them cannot be directly observed by human eyes, and must be found through testing equipment, so we call this kind of pipes sand-hole pipes. The main reasons for sand hole pipes are as f
(1) The hole type does not matchThere are two-roller, three-roller and four-roller weld seam extrusion structures. As long as the combined hole shapes do not match, it is easy to cause scratches on the surface of the tube blank, especially the two-roller structure.There are many factors that cause t